Categories | Gloss Polycarbonate Sheet |
---|---|
Brand Name: | DOBESTY |
Certification: | SGS、REACH、ROSHS |
Place of Origin: | CHINA |
MOQ: | 6 Rolls |
Payment Terms: | T/T |
Supply Ability: | 3000+Rolls+Month |
Delivery Time: | 14 Work Days |
Packaging Details: | 6 Rolls/Plt |
Color: | Transperante |
Light Transmission: | >89% |
Specific Gravity: | 1.2g/cm3 |
Surface Texture: | Polish/Polish |
Surface Tension: | ≥ 36dyn/cm |
Vicat Softening Temperature: | 148℃ |
Permittivity: | 3.1 |
PC6811RQ
Characteristic
Precautions
1. It is forbidden to contact with the surface of fresh cement, acid and alkaline substances.
2. It is forbidden to contact with organic solvents such as benzene, gasoline, carbon tetrachloride, Tianna water, turpentine, or glues or paints containing such components
Description
PC sheet is also called polycarbonate sheet, Kapron sheet. Weak acid resistance, which is made of polycarbonate as the main component and adopts co-extrusion technology CO-EXTRUSION, shows that the PC sheet is resistant to neutral oil, strong acid, durable, and alkali-resistant. It needs to be coated with UV. But the high temperature resistance and good lighting effect PC sunshine board (also known as polycarbonate hollow sheet, glass capron sheet, PC hollow sheet) is processed with high-performance engineering plastic ---- polycarbonate (PC) resin It has the characteristics of high transparency, light weight, impact resistance, sound insulation, heat insulation, flame retardance, and aging resistance. It is a high-tech, extremely comprehensive performance, energy-saving and environmentally friendly plastic sheet, and is a widely used plastic building in the world Materials, there are advantages that other building decoration materials (such as glass, plexiglass, etc.) can not match.
Typical Property Values
Property | Testing Method | Testing Condition | Units | Value |
Physical | ||||
Specific Gravity | ISO 1183 | —— | G/cm3 | 1.2 |
Light Transmission | ASTM D1003 | —— | % | >89 |
Water Absorption Equilibrium | ASTM D570 | 24 Hours | % | 0.35 |
Mechanical | ||||
Tensile Strength | ISO527 | —— | Mpa | 60 |
Tensile Modulus | ISO527 | Mpa | 2400 | |
Flexural Modulus | ISO178 | Mpa | 92 | |
Temperature Resistance | ||||
Vicat Softening Temperature | ISO306 | ℃ | 148 | |
Thermal expansivity | ISO11359 | /℃ | 6.5*10-5 | |
Electrical | ||||
Permittivity | IEC60250 | —— | 3.1 | |
Voltage test | IEC60243 | KV/mm | 30 | |
Volume Resistivity | ICE60093 | 25℃,50%RH | Ω.cm | 1016 |
Surface Resistivity | ICE60093 | 25℃,50%RH | Ω | 1017 |
Gaute Variation | >0.5mm ±3% | |||
0.25—0.5mm ±5% | ||||
0.1—0.25mm ±10% | ||||
≤0.1mm ±0.008mm |
Note: The above figures are typical values obtained under standard methods and should not be construed as unsteady application conditions.
Application
Wide used in such as:the hat,sunglass,windows,aviation sheet,lighting,electroplating,vacuum forming,dyeing,etc.