| Categories | Optical Lenses |
|---|---|
| Brand Name: | FSO |
| Model Number: | FSOOM-1 |
| Certification: | ISO 9001 |
| Place of Origin: | China |
| MOQ: | 1 pcs |
| Price: | Negotiation |
| Payment Terms: | T/T |
| Supply Ability: | 10000pcs/month |
| Delivery Time: | As customer's requirement |
| Packaging Details: | Standard |
| Material: | MgF2 or CaF2,MgF2 |
| Size: | 1-250 mm |
| Surface quality: | 60/40 or better |
| Dimention Tolerance: | +/-0.1mm |
| Thickness Tolerance: | ±0.02mm |
| Bevel: | 0.1-0.3mm X45 Degree |
| Clear Aperture: | >85%>90% |
| Coating: | Uncoated, AR, HR, Beamsplitter ect |
| Surface Flatness: | λ/10@632.8 nm |
| Paramllelism: | +/-3', +/-30'' |
UV Grade Magnesium Fluoride(MgF2) Optical Plano Convex(PCX)
Lenses,MgF2 Optics
Magnesium Fluoride(MgF2 window) is used for optical elements in the
infrared where extreme ruggedness and durability is required. Its
useful transmission range is 0.11 μm - 8.5 μm. Irradiation does not
lead to color centers. Magnesium fluoride is a rugged, hard
material which is resistant to thermal and mechanical shock.
Considerable mechanical shock is needed to cause cleavage. So high
purity and polish is extremely critical during processing.
Specifications
| Diameter | 0.2-300mm |
| Diameter tolerance | +/-0.1mm or +/-0.02mm |
| Thickness | 0.10-100mm |
| Thickness tolerance | ± 0.1mm or +/-0.02mm |
| Surface quality (scratch & dig) | 60/40, 40/20 or better |
| Surface accuracy | λ/10, λ/2, λ |
| Clear Aperture | >85%, >90% |
| Parallelism | +/-3' ,+/-30'' |
| Bevel | 0.1~0.3mm×45 degree |
| coating | AR, HR or upon customer request( UV, VIS, IR) |
MgF2 crystal shows good optical and thermal-mechanical properties. It
is widely used for optical elements such as windows, lenses and
prisms in the ultraviolet and infrared optical system where extreme
durability is required. Its useful transmission range is
0.11μm~7.5μm. Because of its birefringence caused by optical
anisotropy, MgF2 is also used as polarization optics.
Optical properties
| Transmission Range | 0.11 to 7 microns |
| Refractive Index (table below) | 1.37608 at 0.7 microns |
| Reflection Loss | 5.2% at 0.6 microns (2 surfaces) |
| Absorption Coefficient | 40 x 10-3 cm-1 at 2.7nm |
| Restrahlen Peak | 20nm |
| dN/dT | 2.3 (parallel) & 1.7 x 10-6 (perp) at 0.4nm |
| dN/d | 1.4nm |
Physical properties
| Density | 3.18 gm/cm3 |
| Melting Point | 1255oC |
| Thermal Conductivity | 0.3 Wm-1K-1 at 300K |
| Thermal Expansion | 13.7 (para) & 8.9 (perp) x 10-6/K |
| Hardness | Knoop 415 |
| Specific Heat Capacity | 1003 J Kgm-1K-1 |
| Dielectric Constant | 4.87 (para) 5.45 (perp) at 1MHz |
| Youngs Modulus (E) | 138.5 GPa |
| Shear Modulus (G) | 54.66 GPa |
| Bulk Modulus (K) | 101.32 GPa |
| Elastic Coefficient | C11=140 C12=89 C44=57 C13=63 C66=96 |
| Apparent Elastic Limit | 49.6 MPa (7200 psi) |
| Poisson Ratio | 0.276 |
Chemical properties
| Solubility | 0.0002g/100g water |
| Molecular Weight | 62.32 |
| Class/Structure | Tetragonal, can cleave on C-axis |
|
Calcium Fluoride(CaF2) Optical Grade Plano Convex Lenses,CaF2 Optics
Custom Optical Grade Sapphire Glass Lenses with Coating
Zinc Sulfide(ZnS) FLIR Grade Optical Glass Dome Lenses / Zinc Sulfide Optical Windows
Wholesale Optical Grade Zinc Selenide(ZnSe) Plano-Convex (PCX) CO2 Laser lenses
Infrared Optical Grade Germanium(Ge) Plano Convex Lens,Germanium Optics
Silicon Optical Grade Plano-Convex Lenses Manufacturer AR Coated